Raman spectroscopy and structure of selected Ga2O3-CaO-P2O5 glasses
Maria Chromcikova  1@  , Jana Holubova  2@  , Jan Machacek  3@  , Zdenek Cernosek  2@  , Marek Liska  1@  
1 : Vitrum Laugaricio – Joint Glass Center of IIC SAS, TnU AD, and FChPT STU  (VILA)
Študentská 2, Trenčín, SK-91150 -  Slovakia
2 : Department of General and Inorganic Chemistry, Faculty of Chemical technology, University of Pardubice
Študentská 573, CZ-532 10 Pardubice -  Czech Republic
3 : Faculty of Chemical Technology, University of Chemical Technology
Technická 5, CZ-16628 Prague -  Czech Republic

The structure of xGa2O3·(50-x)CaO·50P2O5 (x = 0, 5, 10, 15, and 20) glasses was investigated by 31P MAS NMR and Raman spectroscopy. With increasing content of Ga2O3 the shift form metaphosphate (Q2) to pyrophosphate (Q1) Q-units was found by the 31P MAS NMR. Only small amount (approx. 3%) of orthophosphate Q0 units was observed for x = 15, and 20. The principal component analysis of experimental Raman spectra identified two independent components. Multivariate Curve Resolution analysis (MCR) of experimental Raman spectra performed for two components resulted in corresponding loadings and scores. Spectral decomposition by the method of Malfait was performed using the molar amount of Q2 and Q1 units as composition data. Such way the partial Raman (PRS) spectra of Q2 and Q1 structural units were obtained. In both cases (i.e. MCR and Malfait decomposition) the experimental spectra were reproduced with excellent accuracy. Moreover the normalized PRS are practically identical with the corresponding normalized loadings obtained by MCR. As far as the scores obtained by MCR are not unique, the method of scores adjustment was proposed. This way the good coincidence between the adjusted scores and molar amounts of considered Q-units (i.e. Q2 and Q1) was obtained. The obtained results confirmed the structural information acquired from 31P MAS NMR.